XPREG® XA120 is a structural epoxy adhesive film used to provide a high strength bond between composite laminate and core materials such as aluminium honeycomb, Nomex® or foam core (such as Rohacell®). This film adhesive can also be used to provide additional resin around bonding fasteners and inserts or underneath peel-ply when using peel-ply to provide a secondary bonding surface.
Warning: Last items in stock!
Availability date:
XPREG® XA120 Prepreg Adhesive Film, 150g (1250mm) - 1m Roll
XPREG® XA120 is a structural epoxy adhesive film used to provide a high strength bond between composite laminate and core materials such as aluminium honeycomb, Nomex® or foam core (such as Rohacell®). This film adhesive can also be used to provide additional resin around bonding fasteners and inserts or underneath peel-ply when using peel-ply to provide a secondary bonding surface.
Recipient :
* Required fields
or Cancel
XPREG® XA120 is a structural epoxy adhesive film used to provide a high strength bond between composite laminate and core materials such as aluminium honeycomb, Nomex® or foam core (such as Rohacell®). This film adhesive can also be used to provide additional resin around bonding fasteners and inserts or underneath peel-ply when using peel-ply to provide a secondary bonding surface.
XA120's advanced, toughened epoxy formulation results in outstanding bond and peel-strength at the very forefront of adhesive film performance.
This prepreg resin film is suitable for autoclave, oven or heated platen press cure. XA120 cannot be cured at room temperature.
Features
Cure Cycle
The recommended cure cycle for XA120 is 8hrs at 90°C (ramp rate 2°C/min) which will result in a Tg of 100°C. Where the maximum Tg is required, a post cure of 120°C for 1hr should be followed (ramp rate 0.3°C/min).
See datasheet for full details including alternative cure cycles from 80°C.
Compatibility with XPREG® Prepregs
XA120 is fully compatible with XPREG° XC110 (out-of-autoclave) and XC130 (autoclave) cure prepregs and can be co-cured with these prepreg systems or used in a '2-shot' process to provide secondary bonding onto laminates made using these systems (peel-ply finish or surface preparation would be required).
No customer reviews for the moment.
XPREG® XC110 is an advanced out of autoclave prepreg carbon fibre surface...
OUT OF AUTOCLAVE | COMPONENT | SURFACE PLY | Advanced Prepreg carbon fibre...
AUTOCLAVE/OOA CURE | COMPONENT | UNIDIRECTIONAL | Toughened unidirectional...
XPREG® XC130 is an epoxy-based component autoclave prepreg carbon fibre...